4.5%Magnesium D300 Spool MIG Er5556 Aluminum Welding Wire

KD-ER5556

Description: 

ER5556 is a king of aluminium magnesium alloy welding wire which contains 5%magnesium and 0.8%manganese, and slight Chrome and titanium. It is used for welding aluminium alloy structure widely which requested higher strength, excellent crack resistance, higher bending strength and  corrosion resistance.

Characteristic:

It has the features of excellent welding performance,fine and  Bright welding appearance,electric arc stable and splashes slightly.

Application:

Applying for welding 5XXX series aluminium magnesium alloy. Eg: 5083aluminum alloy and 5456aluminum alloy, it is widely used for the industry of military production ,storage tank, shipbuilding, marine engineering,aviation etc..

Chemical composition(%)
 

Element	Si	Fe	Cu	Mn	Mg	Cr	Zn	Ti	Al	Be	others
GB/T Standard	≤0.25	≤0.40	≤0.10	0.5-1.0	4.7-5.5	0.05-0.20	≤0.25	0.05-0.2	margin	≤0.0003	single≤0.05  total≤0.15
Sample test value	0.05	0.11	0.007	0.81	5.12	0.09	0.005	0.09	margin	0.0001	/

Physical properties of deposited metal
 

Tensile Strength Rm/MPa	 Yield strength Rel/p0.2 MPa	Percentages elongation after fracture A (%)	 Shield gas
286	145	19	100%Ar
Welding Method:MIG

Mechanical property physical Properties
 

The range of melting temperature(ºC)	 Density(g/mm³)
572-633	2.65
Dry elongation: 15-25mm
Shield gas:  99.99%Ar,  75%Ar+25%He,  50%Ar+50%He

Welding reference parameters(Welding Method:MIG:DC+  TIG:AC)
 

MIG	Welding wire diameter(mm)	1.2Â	1.6Â	2.0Â
	 Welding current(A)	180-300	200-400	240-450
	 Welding voltage(V)	18-26	20-28	22-32
TIG	 Welding wire diameter(mm)	1.6-2.5	2.5-4.0	4.0-5.0
	 Welding current(A)	150-250	200-320	220-400

Attention 

1. Please remove the oxide film and grease of edge-weld and surface of welding wire from the welding parts Strictly , or it will form lack of fusion on welding line and cause blow hole, slag inclusion and such other defects.                                                                                        

1. To keep weld penetration without collapsing, please hold the melt metals by cushioning when weld the wire

Details of products :

KD-ER5556

Description: 

ER5556 is a king of aluminium magnesium alloy welding wire which contains 5%magnesium and 0.8%manganese, and slight Chrome and titanium. It is used for welding aluminium alloy structure widely which requested higher strength, excellent crack resistance, higher bending strength and  corrosion resistance.

Characteristic:

It has the features of excellent welding performance,fine and  Bright welding appearance,electric arc stable and splashes slightly.

Application:

Applying for welding 5XXX series aluminium magnesium alloy. Eg: 5083aluminum alloy and 5456aluminum alloy, it is widely used for the industry of military production ,storage tank, shipbuilding, marine engineering,aviation etc..

Chemical composition(%)
 

Element	Si	Fe	Cu	Mn	Mg	Cr	Zn	Ti	Al	Be	others
GB/T Standard	≤0.25	≤0.40	≤0.10	0.5-1.0	4.7-5.5	0.05-0.20	≤0.25	0.05-0.2	margin	≤0.0003	single≤0.05  total≤0.15
Sample test value	0.05	0.11	0.007	0.81	5.12	0.09	0.005	0.09	margin	0.0001	/

Physical properties of deposited metal
 

Tensile Strength Rm/MPa	 Yield strength Rel/p0.2 MPa	Percentages elongation after fracture A (%)	 Shield gas
286	145	19	100%Ar
Welding Method:MIG

Mechanical property physical Properties
 

The range of melting temperature(ºC)	 Density(g/mm³)
572-633	2.65
Dry elongation: 15-25mm
Shield gas:  99.99%Ar,  75%Ar+25%He,  50%Ar+50%He

Welding reference parameters(Welding Method:MIG:DC+  TIG:AC)
 

MIG	Welding wire diameter(mm)	1.2Â	1.6Â	2.0Â
	 Welding current(A)	180-300	200-400	240-450
	 Welding voltage(V)	18-26	20-28	22-32
TIG	 Welding wire diameter(mm)	1.6-2.5	2.5-4.0	4.0-5.0
	 Welding current(A)	150-250	200-320	220-400

Attention 

1. Please remove the oxide film and grease of edge-weld and surface of welding wire from the welding parts Strictly , or it will form lack of fusion on welding line and cause blow hole, slag inclusion and such other defects.                                                                                        

1. To keep weld penetration without collapsing, please hold the melt metals by cushioning when weld the wire

Details of products :

Helper has designed different filler series for small scale producer, medium sized business, and industrial enterprises,such as Vacuum Filler ,Piston Stuffers. 

---The vane cell feed system, together with vacuum pumping system, guarantees a long service life and the highest product quality. 

---Mechanical filler is newly designed by our feeding technical team and it represents a new beginning of Chinese mechanical filling machine. 

---Pneumatic filler is the most economical solution for the beginning of small scale producer with frequent changes in the product range. 

Sausage Linking System,Sausage Hanging System:

The sausage linking and hanging system is the advanced solution to hang the sausages immediately after twisting-off. The workers handle easily the hanged sausages to smoking step by using a hanging stick. A simple twist linking device is also available to the filling machine to realize automatic twisting products production.

Filling And Linking Technology

Automatic Sausage Stuffer,Vacuum Filler,Sausage Linking System,Sausage Hanging System,Piston Stuffers

Shijiazhuang Helper Food Machinery Co., Ltd. , https://www.ihelpergroup.com